파쇄기 날 재질: CPM 10V vs 카바이드 인레이 (2026)

In industrial shredding, Wear Cost Per Ton is a key performance indicator (KPI). A set of D2 blades costing \$2,000 that lasts 500 hours (\$4/hr) is far more expensive than a set of CPM 10V blades costing \$6,000 that lasts 4,000 hours (\$1.50/hr). This guide explores the advanced metallurgy options beyond standard tool steel.

관련 장비: 단일 샤프트 파쇄기.

1. The Baseline: D2 / SKD11

• 구성: 1.5% 탄소, 12% 크롬.
• 성능: The industry standard for general plastics.
• Limitation: Large carbide structures in the steel matrix are prone to “pull-out” (micro-chipping) when processing abrasive materials like glass-filled nylon or dirty film.

2. The Upgrade: CPM 10V (Powder Metallurgy)

Crucible Particle Metallurgy (CPM) creates a steel with a uniform distribution of extremely fine Vanadium Carbides.
* 구성: 2.45% Carbon, 9.75% Vanadium.
* 성능: Vanadium Carbides are harder than Chromium Carbides (Rockwell C 82 vs 66 equivalent).
* Wear Life: Typically 5x to 10x that of D2 in abrasive applications.
* 가장 적합한: Glass-reinforced plastics, Paper (high silica content), contaminated film.
* 강인함: Surprisingly good due to the fine grain structure, resisting shock better than standard D2.

3. The Extreme: Cemented Carbide Inlays

Tungsten Carbide is not steel; it is a ceramic-metal composite.
* 애플리케이션: Brazing a solid carbide strip onto a steel carrier body.
* 경도: 1600 Vickers (~90 HRC).
* Wear Life: Extremely long. Can act as “permanent” blades in some soft applications.
* Fatal Flaw: Brittleness. If a steel bolt or hammer enters the shredder, the carbide can shatter like glass.
* 가장 적합한: Tire recycling (wire-free), Carpet recycling (CaCO3 backing).

4. Hardfacing: The “Armored” Rotor

Wear doesn’t just happen to the knives; the rotor body wears too.
* Technique: Welding a matrix of Tungsten Carbide particles onto the rotor surface.
* Pattern: “Waffle” or “Cross-hatch” patterns trap material, allowing plastic-on-plastic wear instead of plastic-on-steel.
* 유지: Hardfacing is typically re-applied during scheduled overhauls; the interval depends on abrasion, uptime, and maintenance strategy.

5. The “Free” Upgrade: Cryogenic Treatment

Deep Cryogenic Treatment (DCT) involves cooling the blades to -196°C (-320°F) for 24+ hours after heat treatment.
* Science: Transforms soft “Retained Austenite” into hard “Martensite.”
* 결과: Increases abrasive wear resistance by 20-30% and relieves internal stresses (reducing cracking risk).
* 비용: Negligible (<5% of blade cost). Always specify Cryo.

Summary Selection Guide